Thermodynamic modeling of the In–Sc and In–Y systems supported by first-principles calculations
J. Min. Metall. Sect. B-Metall. 54 (2) B (2018) 161-167. DOI:10.2298/JMMB171121004H
Full text (pdf)
Export manuscript information:
RIS Format (EndNote, Reference Manager), BibTeX
Abstract
Based on an assessment of the phase equilibria and thermodynamic data in the literature, the thermodynamic modeling of the In-Sc and In-Y systems was carried out by means of the calculation of phase diagram (CALPHAD) method supported by first-principles calculations. The solution phases, i.e., liquid, (In), (αSc), (βSc), (αY) and (βY), were modeled with the substitutional regular solution model. Ten intermetallic compounds, including InSc3, InSc2, In4Sc5, InSc, In2Sc, In3Sc, InY2, InY, In5Y3, and In3Y were described as stoichiometric phases, while In3Y5 was modeled with a sublattice model with respect to its homogeneity range. The enthalpies of formation of the intermetallic compounds at 0 K were computed using firstprinciple calculations and were used as input for the thermodynamic optimization. A set of self-consistent thermodynamic parameters for both the In-Sc and In-Y systems were obtained and the calculated phase diagrams are in good agreement with the experimental data.
Keywords: In-Sc; In-Y; Thermodynamic optimization; First-principles calculation; CALPHAD; Phase diagram
Correspondence Address:
C, Huang, School of Materials Science and
Engineering, Chongqing, China
email: cquthc@cqut.edu.cn
This work is licensed under a
Creative Commons Attribution-
ShareAlike 4.0 International License