Sb recovery from an As pre-removed lead anode slime using a ZnS-Na2CO3 smelting reduction
J. Min. Metall. Sect. B-Metall., 60 (2) (2024) 177-189. DOI:10.2298/JMMB231230017D
Full text (pdf)
Export manuscript information:
RIS Format (EndNote, Reference Manager), BibTeX
Available online 26 September 2024
(Received 30 December 2023; Accepted 27 June 2024)
doiSerbia
Lead anode slime is produced in large quantities during lead electrolysis, which has a high Sb content of 10-50 wt% and can be easily recycled. However, in a general alkaline pressure leaching process for pre-removal of As, Sb was partially converted to Na3SbO4 with high stability. This limited the Sb reduction and recovery in the subsequent Na2CO3 smelting reduction. Considering this fact, ZnS was creatively used as an additive in this study to destroy the stable structure of Na3SbO4 and increase Sb reduction, and meanwhile ZnS was reduced to volatile Zn (g) and recycled. In a certain range, increasing the amount of coke and ZnS increased the Sb yield, and Pb recycling could be accelerated. However, when an excessive amount of ZnS was added, the Sb compounds could be sulfurized and then combined with the generated PbS and Na2S, forming a sodium matte of Na-Pb-Sb-S. This limited the Sb reduction and reduced the Sb yield. Under the optimum conditions of a coke content of 13%, a ZnS/Sb molar ratio of 0.32, a smelting temperature of 1200 °C and a holding time of 90 min, Sb, Pb and Zn yields of up to 94.8%, 96.1% and 98.9%, respectively, were obtained.
Keywords: As pre-removed lead anode slime; Sb recovery; ZnS; Phase transformation; Smelting reduction
Correspondence Address:
X.-Y. Guo; L. Li ,
Central South University, School of Metallurgy and Environment, Changsha, China; Donghua University, College of Environmental Science and Engineering, Shanghai, China;
email: xyguo@csu.edu.cn; tianxiametal1008@dhu.edu.cn
This work is licensed under a
Creative Commons Attribution-
ShareAlike 4.0 International License