L.-H. Zheng, L.-G. Zhang, F.-Y. Zhao, L.-B. Liu, D. Wang, C.-J. Wu

Phase Equilibria of the Al–Co–Er System at 400°C and 600°C

J. Min. Metall. Sect. B-Metall., 57 (3) (2021) 359-370 DOI:10.2298/JMMB210317032Z
Full text (pdf)

Export manuscript information:
RIS Format (EndNote, Reference Manager), BibTeX
Available online 14 June 2021
(Received 17 March 2021; Accepted 14 June 2021)


The 400°C and 600°C isothermal sections of the Al–Co–Er system were studied assisted with X-ray diffraction (XRD), scanning electron microscopy (SEM), and electron probe microanalysis (EPMA) techniques. 18 three-phase fields were identified in the 400°C isothermal section. The maximum solid solubilities of Al in Co3Er and Co2Er were 13.93 at.%, and 16.13 at.%, respectively whereas the maximum solid solubilities of Co in Al2Er, Al2Er3 and AlEr2 were 6.93 at.%, 6.65 at.%, and 6.49 at.%, respectively. The solid solution range of λ is from 22.22 at.% Al to 44.44 at.% Al while the 600°C isothermal section included 20 three-phase fields. The maximum solid solubilities of Al in Co17Er2 and Co7Er2 were 10.17 at.% and 10.24 at.%, respectively. The maximum solid solubilities of Co in Al2Er and Al2Er3 were 3.63 at.% and 2.01 at.%, respectively.

Keywords: Phase Equilibria; Al–Co–Er; Aluminum alloys

Correspondence Address:
L.-G. Zhang,
School of Materials Science and Engineering, Central South University, Changsha, China;,
email: ligangzhang@csu.edu.cn



Creative Commons License
This work is licensed under a
Creative Commons Attribution-
ShareAlike 4.0 International License