Insight on the reduction of copper content in slags produced from the Ausmelt Converting Process

J. Min. Metall. Sect. B-Metall., 57 (2) (2021) 155-162 DOI:10.2298/JMMB201016013Y
Full text (pdf)

Export manuscript information:
RIS Format (EndNote, Reference Manager), BibTeX
Available online 22 January 2021
(Received 16 October 2020; Accepted 15 January 2021)


The reduction of copper content in converting slag using process control is significant to copper smelter. In this study, the slags produced from the Ausmelt Converting Process for copper matte was analyzed using X-ray diffraction and chemical analysis. Thermodynamic calculation and effects of various conditions including the lance submerging depth in molten bath, the molten bath temperature, the addition of copper matte, and airflow rate were carried out to lower the content in the slag. Thermodynamic analysis indicated that the decrease of copper content was achieved by reducing Fe3O4, CuFe2O4, and Cu2O in the slag, decreasing the magnetism of slag and lowering the viscosity of slag, which was feasible at the operating temperature of the molten bath. Experiments showed that the optimal combination of operating conditions were found to be the addition of copper matte between 5000 – 7000 kg/h, a lance airflow rate of 13000-14000 Nm3/h, and a lance submergence depth into the molten bath of 700-900 mm, in which the copper content in the slag was effectively reduced from 22.74 wt. % to 7.70 wt. %. This study provides a theoretical support and technical guidance for promoting the utilization of slags from the Ausmelt Converting Process.

Keywords: Top-blown converting; Copper content in slag; Copper matte; Blister copper; Ausmelt Furnace

Correspondence Address:
B. Cai,
a Kunming University of Science
and Technology, Kunming, China;
b Copper Branch of Yunnan  Tin Company
Limited, Yunnan Gejiu, China;
email: ytcaibing@163.com



Creative Commons License
This work is licensed under a
Creative Commons Attribution-
ShareAlike 4.0 International License