B. Wierzba, D. Serafin, W.J. Nowak, P. Wierzba, A. Ciećko, A. Mazurkow

Diffusion coefficients in multiphase Ni80Cr20-Ti system

J. Min. Metall. Sect. B-Metall., 57 (1) (2021) 137-144 DOI:10.2298/JMMB200311008W
Full text (pdf)

Export manuscript information:
RIS Format (EndNote, Reference Manager), BibTeX
Available online 21 January 2021
(Received 11 March 2020; Accepted 11 January 2021)


In this paper, the reactive diffusion in Ni80C20r–Ti ternary system is discussed at 1173K. The diffusion couple was prepared and annealed for 100 h. The two intermetallic phases and two two-phase zones occurred, namely: Ti2Ni, TiNi, TiNi+Cr, and TiNi3+Cr. Based on the experimental results (molar fractions, thicknesses of the intermetallic phases), the intrinsic diffusion coefficients of all components in each phase were numerically approximated. The Wagner method was used in the pure intermetallic phases. In the two phase zones the approximation was based on the generalized Darken and Wagner methods. The presented methods allowed for determination of the effective diffusion coefficients in each presented phase.

Keywords: Reaction diffusion; Equilibrium; Ni80Cr20–Ti system

Correspondence Address:
D. Serafin,
Faculty of Mechanical Engineering and Aeronautics, Rzeszow University of Technology, Rzeszów, Poland; ,
email: darseraf@gmail.com



Creative Commons License
This work is licensed under a
Creative Commons Attribution-
ShareAlike 4.0 International License