G. Reyes-Castellanos, A. Cruz-Ramírez, V.H. Gutiérrez-Pérez, J.E. Rivera-Salinas, R.G. Sánchez-Alvarado, E. Colin-García

Experimental assessment of the gray cast iron production by inoculant injection

J. Min. Metall. Sect. B-Metall., 57 (1) (2021) 41-51 DOI:10.2298/JMMB200414035R
Full text (pdf)

Export manuscript information:
RIS Format (EndNote, Reference Manager), BibTeX
Available online 15 December 2020
(Received 14 April 2020; Accepted 08 December 2020)
doiSerbia

Abstract

An initial assessment of the gray cast irons production by injecting an inoculant with a conveying gas into a molten iron bath was evaluated at a laboratory scale. A numerical simulation was carried out to determine the hydrodynamic behavior between the inoculant particles injected into the molten iron. It was determined that an optimal interaction between the particles with the molten iron occurred at a lance depth of 7 cm and for the particle sizes fine (211 to 297 μm) and medium (421 to 590 μm), and the residence time was of 0.38 and 0.4 s, respectively. The melting time was calculated at 0.0008 and 0.003 s for the particle sizes fine and medium, respectively. After the injection, the FeSi of the inoculant melted quickly, releasing the elements of the inoculant which interacted with the molten iron and formed oxides and sulfides creating nucleating sites during solidification. The injection technique allowed obtaining a type-A graphite distribution for the fine and medium particle sizes. The number of eutectic cells increased when the inoculant particle size decreased despite of the low graphitisers elements and manganese contents used in the gray cast iron manufacturing.

Keywords: Gray iron; Injection; Inoculant; Eutectic cell; Numerical simulation

Correspondence Address:
A. Cruz-Ramírez,
Instituto Politécnico Nacional – ESIQIE, Metallurgy and Materials Department, Mexico City, Mexico;,
email: alcruzr@ipn.mx

 

 

Creative Commons License
This work is licensed under a
Creative Commons Attribution-
ShareAlike 4.0 International License