W.J. Nowak, B. Wierzba, A. Mazurkow, A. Jaworski, Ł. Krawczyk

Increase of Austenitic Ductile Iron type D5S durability by high temperature pre-treatment

J. Min. Metall. Sect. B-Metall., 56 (3) (2020) 353-360. DOI:10.2298/JMMB191216028N
Full text (pdf)

Export manuscript information:
RIS Format (EndNote, Reference Manager), BibTeX

Abstract

In the present work, a performance of ASTM A439 Austenitic Ductile Iron type D5S at high temperature in the oxidizing environment was investigated. The obtained results revealed that exposure at temperatures 800°C, 850°C, and 900°C resulted in relatively high mass gain and an extensive oxide scale spallation from the samples’ surfaces during cooling. However, the material exposed at 950°C revealed a better oxidation resistance and no oxide scale spallation. The material exposed at 1000°C showed the best oxidation resistance among the studied samples. The surfaces and cross-sectional investigation revealed that the material exposed at 950°C formed mostly Ni/Cr/Mn-mixed protective oxide scale and local formation of Fe-rich nodules. In comparison with the sample exposed at 1000°C, a smaller amount of Fe-rich nodules per area unit was observed and most of the surface was covered by Ni/Cr/Mn-mixed protective scale. The latter was explained by the change in the calculated diffusion coefficients in the alloy for Ni and Fe, namely up to 900°C the diffusion coefficient for Fe was much higher than for Ni, while above 900°C the diffusion coefficient for Ni becomes higher than for Fe. This phenomenon was correlated with a phase transformation from α-Fe into γ-Fe resulting in the diffusion coefficient change.
Keywords: Ductile iron; Oxidation kinetics; Automotive turbine housings; Lifetime modification; Temperature effect

Correspondence Address:
W. J. Nowak,
Department of Materials Science,
Faculty of Mechanical Engineering and Aeronautics,
Rzeszow University of Technology, Rzeszow, Poland
email: w.nowak@prz.edu.pl

Creative Commons License
This work is licensed under a
Creative Commons Attribution-
ShareAlike 4.0 International License