TY - JOUR T2 - Journal of Mining and Metallurgy, Section B: Metallurgy TI - Atmospheric curing of zinc sulfide concentrate by sulfuric acid below 300 ? VL - 58 IS - 3 SP - 345 EP - 353 PY - 2022 DA - 04 October 2022 DO - 10.2298/JMMB220302016D UR - https://doi.org/10.2298/JMMB220302016D AU - Deng, F.-L. AU - Xu, G.-X. AU - Fan, W.-W. AU - Li, S.-N. AU - Ma, R.-X. AD - a School of Metallurgy and Ecological Engineering, University of Science and Technology Beijing, Beijing, PR China; b Tianjin Research Institute for Water Transport Engineering, Ministry of Transport, Tianjin, PR China; c Beijing Key Laboratory of Special Melting and Preparation of High-end Metal Materials, Beijing, PR China; AB - Because the traditional roasting-leaching-electrowinning zinc hydrometallurgy process has a small sulfuric acid sales radius and a high inventory pressure, the process of direct leaching zinc concentrate is gaining popularity, but the pressurized leaching process is a high-pressure condition, which requires strict equipment material and high safety requirements. Furthermore, the atmospheric leaching efficiency is low and generally introduces impurities and chloride ions, which increase the cost of subsequent decontamination. Therefore, a new environmentally friendly hydrometallurgy extraction method of zinc was proposed: an atmospheric pressure medium temperature sulfuric acid curing-leaching process. Under open-air conditions, zinc sulfide concentrate was cured with sulfuric acid at different acid-to-ore ratios and heated to 220 ?~260 ? for a different time, then the cured product was leached. The effects of temperature, curing time, acid-to-ore ratio, and sulfuric acid concentration on the leaching ratio of zinc (hZn) were studied. The results demonstrated that hZn could reach as high as 98.23% under the optimized conditions of temperature 240 ?, curing time 2.5 hours, acid-to-ore ratio 1.4:1, and sulfuric acid concentration 60 wt.%. The leaching residue ratio is 6%, with silicate accounting for the majority of it. The kinetic results support the shrinking core model, which is controlled by an interface chemical reaction with an apparent activation energy of 43.158 kJ/mol. KW - Zinc sulfide concentrate KW - Atmospheric curing KW - Kinetics KW - Shrinking core model N1 - Correspondence Address: S.-N. Li (b), R.-X. Ma (a,c); a School of Metallurgy and Ecological Engineering, University of Science and Technology Beijing, Beijing, PR China; b Tianjin Research Institute for Water Transport Engineering, Ministry of Transport, Tianjin, PR China; c Beijing Key Laboratory of Special Melting and Preparation of High-end Metal Materials, Beijing, PR China; email: shinali1986@126.com; maruixin@ustb.edu.cn; N1 - J. Min. Metall. Sect. B-Metall., 58 (3) (2022) 345-353. doi:10.2298/JMMB220302016D PB - Technical Faculty in Bor SN - 1450-5339 (ISSN) LA - English J2 - J. Min. Metall. Sect. B Metall. M3 - Article ER -